- Fine gràn
- Homogeneous structar
- Àrd dùmhlachd
- Sònraichte tearmach conductivity
- Àrd-meacanaigeach neart
- Proper dealan
- as ìsle tron wettability gu leaghta meatailtean
- Hard uachdar agus deagh flexural strenght
- Resistance gu ceimigeach bleith agus tearmach clisgeadh.
Fine-gràn Sònraichte Graphite FXG-1 | Fine-gràn Sònraichte Graphite FXG-2 | ||||
Notaichean | Aonad | Gealladh luach | Seallaidhean cumanta air luach | Gealladh luach | Seallaidhean cumanta air luach |
Max gràn meud | mm | 0.8 | 0.8 | 0.8 | 0.8 |
tomad dùmhlachd | g / cm3 | ≥1.70 | 1,73 | ≥1.73 | 1,76 |
sònraichte aghaidh | μΩ.m | ≤8.5 | 7.5 | ≤8.0 | 7 |
Lùbach neart | MPA | ≥10.0 | 11 | ≥12.0 | 12.5 |
Compressive neart | MPA | ≥24.0 | 27 | ≥31.0 | 34 |
ìomhaigheach tearmach Condcutivity | W / (MK) | ≥120 | 150 | ≥130 | 160 |
CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.2 | ≤2.5 | 2.1 |
Ash clàr na làraich | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
Notaichean | Aonad | Gealladh luach | Seallaidhean cumanta air luach | Gealladh luach | Seallaidhean cumanta air luach |
Max gràn meud | mm | 2 | 2 | 2 | 2 |
tomad dùmhlachd | g / cm3 | ≥1.58 | 1.6 | ≥1.70 | 1.75 |
sònraichte aghaidh | μΩ.m | ≤11.5 | 10.5 | ≤8.5 | 7.5 |
Lùbach neart | MPA | ≥6.0 | 6.5 | ≥9.0 | 9.5 |
Compressive neart | MPA | ≥18.0 | 18.5 | ≥30.0 | 31 |
Modulus de elasticity | GPa | ≤9.3 | 7.5 | ≤12.0 | 9.5 |
CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.4 | ≤2.5 | 2.3 |
Ash clàr na làraich | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
àrd-ghlan graphite | ||||
Notaichean | Aonad | fuine dà uair | fuine trì ùine | fuine ceithir tursan |
impregnated aon uair | impregnated dà uair | Impregnated trì tursan | ||
gràn meud | mm | ≤325mesh | ≤325mesh | ≤325mesh |
tomad dùmhlachd | g / cm3 | ≥1.68 | ≥1.78 | ≥1.85 |
sònraichte aghaidh | μΩ.m | ≤14 | ≤14 | ≤13 |
Lùbach neart | MPA | ≥25 | ≥40 | ≥45 |
Compressive neart | MPA | ≥50 | ≥60 | ≥65 |
Ash clàr na làraich | % | ≤0.15 | ≤0.1 | ≤0.05 |
Notaichean | Aonad | Isostatic graphite |
gràn meud | μm | 5-22 |
tomad dùmhlachd | g / cm3 | 1.75-1.85 |
sònraichte aghaidh | μΩ.m | 10-15 |
Lùbach neart | MPA | ≥40 |
Compressive neart | MPA | ≥70 |
Chladaich cruas | ≥5 | |
CTE (100-600) ° C | 10-6 / ° C | 3.2-5.2 |
Modulus de elasticity | GPa | 9.5-12.5 |
Q1: Kodi anu kampani AO Hui amapanga kapena malonda?
A1: Mlengi nthawi timathandiza makasitomala athu kugula zinthu zogwirizana monga malonda a.
Q2: Kodi MOQ?
A2. Palibe malire.
Q3: Kodi tiyendera fakitale wanu?
A3: Inde, kulandira nthawi iliyonse, kuwona nkukhulupirira
Q4: Kodi malipiro mawu anu?
A4: Kukambirana
Q5: Kodi gulu lako kuvomereza mwamakonda?
A5: Professional luso magulu ndi akatswiri onse angathe kukwaniritsa inu.
Q6: Kodi mutsimikizira khalidwe liti?
A6: Pakuti processing iliyonse kupanga tili wathunthu dongosolo QC kwa zikuchokera mankhwala ndi thupi properties.After kupanga katundu onse adzayesedwa, ndi satifiketi Tidzakambirana khalidwe kutumizidwa pamodzi ndi katundu.
Q7: Kodi chiwerengero cha malonda kunja?
A7: Lina msika mozungulira 50%; Msika zoweta mozungulira 50%; ndipo tsopano katundu chiwerengero zikuchulukirachulukira.
Q 8: kampani anu amapeleka zitsanzo?
A8: Inde, tikhoza kupereka zitsanzo kwaulere, ndi katundu adzakhala kugwiridwa ndi makasitomala.