Likarolo tse bōpehileng joaloka Graphite
Likarolo tse bōpehileng joaloka Graphite
Likaroloana
- Lithollo tse ntle
- Sebopeho se ts'oanang
- Sekhahla se phahameng
- Ho tsamaisa mocheso hantle haholo
- Matla a phahameng a mechini
- Ho tsamaisa motlakase hantle
- Ho nosetsa hanyane ho litšepe tse qhibilihisitsoeng
- Bokaholimo bo thata le matla a matle a ho kokobela
- Ho hanyetsa khoholeho ea lik'hemik'hale le ho tšoha ha mocheso.
Letšoao la 'mele le la lik'hemik'hale
| Graphite e Ikhethang ea Lithollo tse Ntle FXG-1 | Graphite e Ikhethang ea Lithollo tse Ntle FXG-2 | ||||
| Ntho | Yuniti | Boleng ba tiisetso | Boleng bo tloaelehileng | Boleng ba tiisetso | Boleng bo tloaelehileng |
| Boholo ba lijo-thollo tse kholo | mm | 0.8 | 0.8 | 0.8 | 0.8 |
| Bongata ba bongata | g/cm3 | ≥1.70 | 1.73 | ≥1.73 | 1.76 |
| Khanyetso e itseng | μΩ.m | ≤8.5 | 7.5 | ≤8.0 | 7 |
| Matla a ho kobeha | MPa | ≥10.0 | 11 | ≥12.0 | 12.5 |
| Matla a khatello | MPa | ≥24.0 | 27 | ≥31.0 | 34 |
| Mocheso o Tsamaisang Mocheso | W/(mk) | ≥120 | 150 | ≥130 | 160 |
| CTE(100-600) °C | 10-6/°C | ≤2.5 | 2.2 | ≤2.5 | 2.1 |
| Dikahare tsa molora | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 |
| Ntho | Yuniti | Boleng ba tiisetso | Boleng bo tloaelehileng | Boleng ba tiisetso | Boleng bo tloaelehileng |
| Boholo ba lijo-thollo tse kholo | mm | 2 | 2 | 2 | 2 |
| Bongata ba bongata | g/cm3 | ≥1.58 | 1.6 | ≥1.70 | 1.75 |
| Khanyetso e itseng | μΩ.m | ≤11.5 | 10.5 | ≤8.5 | 7.5 |
| Matla a ho kobeha | MPa | ≥6.0 | 6.5 | ≥9.0 | 9.5 |
| Matla a khatello | MPa | ≥18.0 | 18.5 | ≥30.0 | 31 |
| Modulus ea elasticity | GPa | ≤9.3 | 7.5 | ≤12.0 | 9.5 |
| CTE(100-600) °C | 10-6/°C | ≤2.5 | 2.4 | ≤2.5 | 2.3 |
| Dikahare tsa molora | % | ≤0.3 | 0.09 | ≤0.3 | 0.09 |
Graphite e hloekileng haholo
| graphite e hloekileng haholo | ||||
| Ntho | Yuniti | e besitsoe habeli | e besitsoe hararo | e besitsoe ka makhetlo a mane |
| e kentsoe hang | e kentsoe habeli | E kentsoe ka makhetlo a mararo | ||
| boholo ba lijo-thollo | mm | ≤325mesh | ≤325mesh | ≤325mesh |
| Bongata ba bongata | g/cm3 | ≥1.68 | ≥1.78 | ≥1.85 |
| Khanyetso e itseng | μΩ.m | ≤14 | ≤14 | ≤13 |
| Matla a ho kobeha | MPa | ≥25 | ≥40 | ≥45 |
| Matla a khatello | MPa | ≥50 | ≥60 | ≥65 |
| Dikahare tsa molora | % | ≤0.15 | ≤0.1 | ≤0.05 |
Graphite e sa fetoheng
| Ntho | Yuniti | Graphite e sa fetoheng |
| boholo ba lijo-thollo | μm | 5-22 |
| Bongata ba bongata | g/cm3 | 1.75-1.85 |
| Khanyetso e itseng | μΩ.m | 10-15 |
| Matla a ho kobeha | MPa | ≥40 |
| Matla a khatello | MPa | ≥70 |
| Ho thatafala ha lebōpo | ≥5 | |
| CTE(100-600) °C | 10-6/°C | 3.2-5.2 |
| Modulus ea elasticity | GPa | 9.5-12.5 |
P1: Na ea haukhamphani ea AO HUImoetsi kapa mohoebi?
A1: Moetsi, ka nako e 'ngoe re thusa bareki ba rona ho reka lihlahisoa tse amehang joalo ka mohoebi.
P2: MOQ ke eng?
A2. Ha ho na moedi.
P3: Na re ka etela fektheri ea hau?
A3: Ehlile, rea u amohela neng kapa neng, ho bona ke ho lumela
P4: Melao ea hau ea tefo ke efe?
A4: Puisano
P5: Na khamphani ea hau e amohela mokhoa oa ho iketsetsa lintho?
A5: Lihlopha tsa theknoloji tsa litsebi le baenjiniere bohle ba ka u khotsofatsa.
P6: U netefatsa boleng joang?
A6: Bakeng sa ts'ebetso e 'ngoe le e 'ngoe ea tlhahiso, re na le sistimi e felletseng ea QC bakeng sa sebopeho sa lik'hemik'hale le thepa ea 'mele. Kamora tlhahiso, thepa eohle e tla lekoa, 'me setifikeiti sa boleng se tla romelloa hammoho le thepa.
P7: Ke karolo efe ea khoebo ea kantle ho naha?
A7: 'Maraka oa kantle ho naha o ka ba 50%; 'Maraka oa lehae o ka ba 50%; 'me joale karolo ea thepa e romeloang kantle ho naha e ntse e eketseha.
Q8: Khamphani ea hau e tla fana kadisampole?
A8: E, re ka fana ka disampole mahala, mme thepa e tla etswa ke bareki.