- Fine okuziinkozo
- isakhiwo yohlobo olunye
- mninzi High
- Zintle conductivity thermal
- High amandla ngoomatshini
- lombane Efanelekileyo
- Ubuncinane wettability to zesinyithi otyhidiweyo
- Hard komhlaba kunye strenght elungileyo flexural
- Resistance kukhukuliseko iikhemikhali kunye nokothuka thermal.
Fine-grain okukhethekile Umsizi FXG-1 | Fine-grain okukhethekile Umsizi FXG-2 | ||||
into | Unit | inani isiqinisekiso | ixabiso lohlobo | inani isiqinisekiso | ixabiso lohlobo |
Obukhulu wokudla | mm | 0.8 | 0.8 | 0.8 | 0.8 |
Unizi lolwapho kuyiwa khona | g / cm3 | ≥1.70 | 1.73 | ≥1.73 | 1,76 |
ukumelana ethile | μΩ.m | ≤8.5 | 7.5 | ≤8.0 | 7 |
ukugoba amandla | MPA | ≥10.0 | 11 | ≥12.0 | 12.5 |
amandla Compressive | MPA | ≥24.0 | 27 | ≥31.0 | 34 |
Condcutivity thermal | W / (MK) | ≥120 | 150 | ≥130 | 160 |
CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.2 | ≤2.5 | 2.1 |
Umxholo ash | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
into | Unit | inani isiqinisekiso | ixabiso lohlobo | inani isiqinisekiso | ixabiso lohlobo |
Obukhulu wokudla | mm | 2 | 2 | 2 | 2 |
Unizi lolwapho kuyiwa khona | g / cm3 | ≥1.58 | 1.6 | ≥1.70 | 1,75 |
ukumelana ethile | μΩ.m | ≤11.5 | 10.5 | ≤8.5 | 7.5 |
ukugoba amandla | MPA | ≥6.0 | 6.5 | ≥9.0 | 9.5 |
amandla Compressive | MPA | ≥18.0 | 18.5 | ≥30.0 | 31 |
Modulus of luthambe | uTsvangirai | ≤9.3 | 7.5 | ≤12.0 | 9.5 |
CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.4 | ≤2.5 | 2.3 |
Umxholo ash | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
grafayithi high olunyulu | ||||
into | Unit | kubhakwa kabini | kubhakwa ixesha ezintathu | kubhakwa kane |
buzane kanye | buzane kabini | Buzane kathathu | ||
ubukhulu wokudla | mm | ≤325mesh | ≤325mesh | ≤325mesh |
Unizi lolwapho kuyiwa khona | g / cm3 | ≥1.68 | ≥1.78 | ≥1.85 |
ukumelana ethile | μΩ.m | ≤14 | ≤14 | ≤13 |
ukugoba amandla | MPA | ≥25 | ≥40 | ≥45 |
amandla Compressive | MPA | ≥50 | ≥60 | ≥65 |
Umxholo ash | % | ≤0.15 | ≤0.1 | ≤0.05 |
into | Unit | grafayithi Isostatic |
ubukhulu wokudla | μm | 5-22 |
Unizi lolwapho kuyiwa khona | g / cm3 | 1.75-1.85 |
ukumelana ethile | μΩ.m | 10-15 |
ukugoba amandla | MPA | ≥40 |
amandla Compressive | MPA | ≥70 |
nganeno yobulukhuni | ≥5 | |
CTE (100-600) ° C | 10-6 / ° C | 3.2-5.2 |
Modulus of luthambe | uTsvangirai | 9.5-12.5 |
Q1: Ingaba yakho inkampani AO hui njengomvelisi okanye umrhwebi?
A1: nomakhi, ezinye ixesha ukunceda abaxhasi bethu ukuthenga iimveliso ezifanelekileyo umrhwebi.
Q2: Yintoni MOQ?
A2. Akukho mda.
Q3: Ngaba utyelele mveliso yakho?
A3: Kakade ke, wamkelekile nanini na ixesha, sikholwa ngokubona
Q4: Yiyiphi imigaqo intlawulo yakho?
A4: Ngothethwano
Q5: Ingaba inkampani wakho makakholiswe ulwenziwo?
A5: amaqela iteknoloji yobungcali iinjineli zonke kunokwanelisa kuwe.
Q6: njani akuqinisekisi esemgangathweni?
A6: Inkqubo yonke imveliso, kufuneka inkqubo QC ngokupheleleyo ukubunjwa imichiza kunye nemveliso Physical properties.After, baza kuvavanywa yonke impahla, kunye nesiqinisekiso uza ngenqanawa kunye nempahla.
Umbuzo 7: Yintoni umlinganiselo amashishini?
A7: market Amazwe umalunga nama-50%; Market Domestic umalunga nama-50%; ke ngoku inani kumazwe buyanda.
Q 8: inkampani wakho uya kunika iisampulu?
A8: Ewe, siya kubonelela iisampuli simahla, yaye eJozi kuya kwenziwa ngabaxumi.