Lẹẹdi Special-sókè Parts
Lẹẹdi Special-sókè Parts
Awọn ẹya ara ẹrọ
- Fine ọkà
- isokan be
- Ga iwuwo
- O tayọ gbona iba ina elekitiriki
- Ga darí agbara
- Dara itanna elekitiriki
- kere wettability to ère awọn irin
- Lile dada ati ti o dara flexural strenght
- Resistance si kemikali ogbara ati ki o gbona-mọnamọna.
Ti ara ati kemikali Ìwé
| Itanran-ọkà nigboro lẹẹdi FXG-1 | Itanran-ọkà nigboro lẹẹdi FXG-2 | ||||
| ohun kan | Unit | lopolopo iye | aṣoju iye | lopolopo iye | aṣoju iye |
| Max ọkà iwọn | mm | 0.8 | 0.8 | 0.8 | 0.8 |
| olopobobo iwuwo | g / cm3 | ≥1.70 | 1.73 | ≥1.73 | 1.76 |
| Specific resistance | μΩ.m | ≤8.5 | 7.5 | ≤8.0 | 7 |
| atunse agbara | MPA | ≥10.0 | 11 | ≥12.0 | 12.5 |
| Compressive agbara | MPA | ≥24.0 | 27 | ≥31.0 | 34 |
| gbona Condcutivity | W / (mk) | ≥120 | 150 | ≥130 | 160 |
| CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.2 | ≤2.5 | 2.1 |
| Ash akoonu | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
| ohun kan | Unit | lopolopo iye | aṣoju iye | lopolopo iye | aṣoju iye |
| Max ọkà iwọn | mm | 2 | 2 | 2 | 2 |
| olopobobo iwuwo | g / cm3 | ≥1.58 | 1.6 | ≥1.70 | 1.75 |
| Specific resistance | μΩ.m | ≤11.5 | 10.5 | ≤8.5 | 7.5 |
| atunse agbara | MPA | ≥6.0 | 6.5 | ≥9.0 | 9.5 |
| Compressive agbara | MPA | ≥18.0 | 18.5 | ≥30.0 | 31 |
| Modulus ti elasticity | GPA | ≤9.3 | 7.5 | ≤12.0 | 9.5 |
| CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.4 | ≤2.5 | 2.3 |
| Ash akoonu | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
Ga funfun lẹẹdi
| ga funfun lẹẹdi | ||||
| ohun kan | Unit | ndin lemeji | ndin mẹta akoko | ndin merin ni igba |
| impregnated ni kete ti | impregnated lemeji | Impregnated ni igba mẹta | ||
| ọkà iwọn | mm | ≤325mesh | ≤325mesh | ≤325mesh |
| olopobobo iwuwo | g / cm3 | ≥1.68 | ≥1.78 | ≥1.85 |
| Specific resistance | μΩ.m | ≤14 | ≤14 | ≤13 |
| atunse agbara | MPA | ≥25 | ≥40 | ≥45 |
| Compressive agbara | MPA | ≥50 | ≥60 | ≥65 |
| Ash akoonu | % | ≤0.15 | ≤0.1 | ≤0.05 |
Isostatic lẹẹdi
| ohun kan | Unit | Isostatic lẹẹdi |
| ọkà iwọn | μm | 5-22 |
| olopobobo iwuwo | g / cm3 | 1.75-1.85 |
| Specific resistance | μΩ.m | 10-15 |
| atunse agbara | MPA | ≥40 |
| Compressive agbara | MPA | ≥70 |
| tera líle | ≥5 | |
| CTE (100-600) ° C | 10-6 / ° C | 3.2-5.2 |
| Modulus ti elasticity | GPA | 9.5-12.5 |
Q1: Se rẹ ile-AO Hui a olupese tabi onisowo?
A1: olupese, diẹ ninu awọn akoko ti a ran wa oni ibara lati ra ti o yẹ awọn ọja bi a onisowo.
Q2: Kini MOQ?
A2. Ko si aropin.
Q3: Le a be rẹ factory?
A3: Dajudaju, gbà ni eyikeyi akoko, ri ti wa ni onigbagbọ
Q4: Kini rẹ owo ofin?
A4: onisowo
Q5: Ti wa ni ile-gba isọdi?
A5: Professional ọna ti egbe ati Enginners gbogbo le ni itẹlọrun o.
Q6: Bawo ni o ṣe ẹri didara?
A6: Fun gbogbo gbóògì processing, a ni pipe QC eto fun awọn kemikali tiwqn ati ara properties.After gbóògì, gbogbo ẹrù yoo ti ni idanwo, ati awọn didara ijẹrisi yoo wa ni bawa pẹlú pẹlu de.
Q7: Kini o yẹ ti odi owo?
A7: Abroad oja ni ayika 50%; Abele oja ni ayika 50%; ki o si bayi okeere o yẹ wa ni npo.
Q 8: Your ile yoo pese awọn ayẹwo?
A8: Bẹẹni, a le pese awọn ayẹwo fun free, ati awọn ẹru yoo wa ni agbeyewo nipa ibara.