- Fine okusanhlamvu
- isakhiwo homogeneous
- ukuminyana High
- Excellent conductivity ezishisayo
- High amandla mechanical
- Proper conductivity kagesi
- Minimum wettability ukuba izinsimbi oncibilikisiwe
- Hard surface futhi strenght ezinhle flexural
- Ukumelana ukuguguleka zamakhemikhali ukushaqeka ezishisayo.
Fine-okusanhlamvu Specialty Graphite FXG-1 | Fine-okusanhlamvu Specialty Graphite FXG-2 | ||||
Into | iyunithi | isiqinisekiso Inani | Inani ejwayelekile | isiqinisekiso Inani | Inani ejwayelekile |
Max usayizi okusanhlamvu | mm | 0.8 | 0.8 | 0.8 | 0.8 |
Bulk ukuminyana | g / cm3 | ≥1.70 | 1.73 | ≥1.73 | 1,76 |
ukumelana Specific | μΩ.m | ≤8.5 | 7.5 | ≤8.0 | 7 |
ukugoba amandla | MPA | ≥10.0 | 11 | ≥12.0 | 12.5 |
amandla compressive | MPA | ≥24.0 | 27 | ≥31.0 | 34 |
Condcutivity Thermal | W / (Mk) | ≥120 | 150 | ≥130 | 160 |
CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.2 | ≤2.5 | 2.1 |
Ash okuqukethwe | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
Into | iyunithi | isiqinisekiso Inani | Inani ejwayelekile | isiqinisekiso Inani | Inani ejwayelekile |
Max usayizi okusanhlamvu | mm | 2 | 2 | 2 | 2 |
Bulk ukuminyana | g / cm3 | ≥1.58 | 1.6 | ≥1.70 | 1.75 |
ukumelana Specific | μΩ.m | ≤11.5 | 10.5 | ≤8.5 | 7.5 |
ukugoba amandla | MPA | ≥6.0 | 6.5 | ≥9.0 | 9.5 |
amandla compressive | MPA | ≥18.0 | 18.5 | ≥30.0 | 31 |
Modulus okunwebeka | GPA | ≤9.3 | 7.5 | ≤12.0 | 9.5 |
CTE (100-600) ° C | 10-6 / ° C | ≤2.5 | 2.4 | ≤2.5 | 2.3 |
Ash okuqukethwe | % | ≤0.3 | 0,09 | ≤0.3 | 0,09 |
okusezingeni eliphezulu graphite okumsulwa | ||||
Into | iyunithi | wabhaka kabili | wabhaka ezintathu isikhathi | wabhaka kane |
elifakwe kanye | elifakwe kabili | Elifakwe kathathu | ||
usayizi okusanhlamvu | mm | ≤325mesh | ≤325mesh | ≤325mesh |
Bulk ukuminyana | g / cm3 | ≥1.68 | ≥1.78 | ≥1.85 |
ukumelana Specific | μΩ.m | ≤14 | ≤14 | ≤13 |
ukugoba amandla | MPA | ≥25 | ≥40 | ≥45 |
amandla compressive | MPA | ≥50 | ≥60 | ≥65 |
Ash okuqukethwe | % | ≤0.15 | ≤0.1 | ≤0.05 |
Into | iyunithi | graphite Isostatic |
usayizi okusanhlamvu | μm | 5-22 |
Bulk ukuminyana | g / cm3 | 1.75-1.85 |
ukumelana Specific | μΩ.m | 10-15 |
ukugoba amandla | MPA | ≥40 |
amandla compressive | MPA | ≥70 |
Shore ubulukhuni | ≥5 | |
CTE (100-600) ° C | 10-6 / ° C | 3.2-5.2 |
Modulus okunwebeka | GPA | 9.5-12.5 |
Q1: Er þinn fyrirtæki AO Hui framleiðandi eða kaupmaður?
A1: Framleiðandi, sumir tími að við hjálpum viðskiptavinum okkar að kaupa viðkomandi vörur sem kaupmaður.
Q2: Hvað er MOQ?
A2. Engin takmörkun.
Q3: Getum við heimsækja verksmiðju þinn?
A3: Auðvitað, velkomin hvenær sjá er að trúa
Q4: Hvað er greiðsluskilmála?
A4: Samningaviðræður
Q5: Er fyrirtækið þitt við customization?
A5: Professional tækni lið og verkfræðingar allir geta fullnægja þér.
Q6: Hvernig tryggja gæði?
A6: Fyrir hvert vinnslu, höfum við lokið QC kerfi fyrir efnasamsetningu og Physical properties.After framleiðslu, allar vörur verður að prófa, og gæði vottorð verður flutt með vörur.
Q7: Hvað er hlutfall erlendis fyrirtæki?
A7: erlendis markaði um 50%; Innlendum markaði um 50%; og nú útflutning hlutfall fer vaxandi.
Q 8: Fyrirtækið þitt myndi veita sýni?
A8: Já, gætum við framboð sýni ókeypis og fragt verður ráðist af viðskiptavinum.